In manufacturing parts by the hot pressing method, composite parts with different formulations can be used especially for baking at high temperatures and pressure. This method is used for high- volume and expensive parts due to the high price of molding. SMC-BMC resins are suitable for making composite parts with high surface quality, heat resistance, and chemical resistance.
Type | Product | Solid Contet (%) | Viscosity@25 c (MPa.S) | Color (Gardner) | Acid Value | Gel time (Min) | Hardness (Barcol) | Tensile Strength (MPa) | Flexural strength (MPa) | HDT(°C) |
ortho
Ortho Ortho | 0-730 | 63 | 450-700 | <2 | <10-14 | 15-35 | 40min | 60min | 120 | 65 |
0-731 | 63 | 700-1000 | - | 20 | 18-35 | 40min | 65min | 120 | 65 | |
Iso | I-760 | 64 | 600-900 | <2 | <20 | 15-35 | 45min | 70min | 130 | 70 |